I don't think I'm going to be building any K-41 Carbon Fibre towers anytime soon.
My re-launch into R/C is keeping most of my hobby time busy.
__________________
When in doubt, WHACK the GAS and DITCH the brake !!! Yes, there is such a thing as NORMAL, if you have to ask what is "NORMAL" , you probably aren't ! Failure may not be an OPTION, but it is ALWAYS a POSSIBILITY. ALL systems are GO for MAYHEM, CHAOS, and HAVOC ! |
#12
|
||||
|
||||
I did a carbon fibre tower for an Estes MR not too long ago. I would recommend against it. I tried CA and epoxy and neither one bonds adequately in my opinion. I feel fairly certain that the tower will be gone after its first launch. Now if you're building a hangar queen, that's a different matter.
Joe |
#13
|
||||
|
||||
I have had god luck bonding carbon fibre with epoxy, but it has to be 'scuffed' with sandpaper to give the epoxy area to 'bite' into.
__________________
When in doubt, WHACK the GAS and DITCH the brake !!! Yes, there is such a thing as NORMAL, if you have to ask what is "NORMAL" , you probably aren't ! Failure may not be an OPTION, but it is ALWAYS a POSSIBILITY. ALL systems are GO for MAYHEM, CHAOS, and HAVOC ! |